商品描述價格說明聯系我們加工級別注塑級、吹塑級牌號RE19045用途級別食品級、汽車部件、板材級、運動器材、瓶蓋料、家電部件、電動工具配件、薄壁制品類型標準料是否進口是廠家(產地)美國杜邦特性級別透明級、、耐低溫、標準級、耐水解、、耐老化、耐候、抗靜電、抗化學性、高強度、高流動、高抗沖、高滑動、高光澤、高剛性銷售方式品牌經銷產品規格25KG/包產地美國品名美國杜邦PET產品特性阻燃可售賣地全國DuPont Performance Polymers Rynite? RE19045PET (Unverified Data**)Polyethylene Terephthalate (PET), 40% Glass ReinforcedDuPont Performance Polymers產品說明：Rynite? RE19045is a 40% glass and mineral reinforced, flame retardant, polyethylene terephthalate black resin.Information provided by DuPont Performance Polymers物性信息：物理性能額定值 (公制)額定值 (英制)測試方法密度1.73 g/cc0.0625 lb/in3ISO 1183線性成型收縮率,Flow0.0020 cm/cm@Thickness 2.00 mm0.0020 in/in@Thickness 0.0787 inISO 294-4線性成型收縮率，橫向0.0090 cm/cm@Thickness 2.00 mm0.0090 in/in@Thickness 0.0787 inISO 294-4化合物熔體指數70 g/10 min@Load 5.00 kg, Temperature 280 °C70 g/10 min@Load 11.0 lb, Temperature 536 °Fcm3/10 min; ISO 1133機械性能額定值 (公制)額定值 (英制)測試方法抗張強度(斷裂)110 MPa@Temperature 23.0 °C16000 psi@Temperature 73.4 °FISO 527伸長率 (斷裂)1.7 %@Temperature 23.0 °C1.7 %@Temperature 73.4 °FISO 527拉伸模量11.0 GPa@Temperature 23.0 °C1600 ksi@Temperature 73.4 °FISO 527彎曲強度170 MPa@Temperature 23.0 °C24700 psi@Temperature 73.4 °FISO 178彎曲模量9.70 GPa@Temperature 23.0 °C1410 ksi@Temperature 73.4 °FISO 178簡支梁缺口沖擊強度0.650 J/cm2@Temperature 23.0 °C3.09 ft-lb/in2@Temperature 73.4 °FISO 179/1eA電氣性能額定值 (公制)額定值 (英制)測試方法體積電阻率5.00e+14 ohm-cm@Temperature 23.0 °C5.00e+14 ohm-cm@Temperature 73.4 °FIEC 60093表面電阻>= 1.00e+15 ohm@Temperature 23.0 °C>= 1.00e+15 ohm@Temperature 73.4 °FIEC 60093介電強度32.0 kV/mm@Temperature 23.0 °C813 kV/in@Temperature 73.4 °FIEC 60243-1熱性能額定值 (公制)額定值 (英制)測試方法線形熱膨脹系數 - 流動500 μm/m-°C@Temperature -40.0 - 23.0 °C278 μin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-2500 μm/m-°C@Temperature 23.0 - 55.0 °C278 μin/in-°F@Temperature 73.4 - 131 °FISO 11359-1/-2500 μm/m-°C@Temperature 55.0 - 160 °C278 μin/in-°F@Temperature 131 - 320 °FISO 11359-1/-2線性熱膨脹系數,橫向流動61.0 μm/m-°C@Temperature -40.0 - 23.0 °C33.9 μin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-278.0 μm/m-°C@Temperature 23.0 - 55.0 °C43.3 μin/in-°F@Temperature 73.4 - 131 °FISO 11359-1/-2110 μm/m-°C@Temperature 55.0 - 160 °C61.1 μin/in-°F@Temperature 131 - 320 °FISO 11359-1/-2熔融溫度247 °C477 °F10°C/min; ISO 11357-1/-3載荷下熱變形溫度(1.8 MPa)214 °C417 °FISO 75-1/-2玻璃化轉變溫度，Tg100 °C212 °F10°C/min; ISO 11357-1/-2UL RTI155 °C@Thickness 0.810 mm311 °F@Thickness 0.0319 inUL 746BUL RTI，機械沖擊155 °C@Thickness 0.810 mm311 °F@Thickness 0.0319 inUL 746BUL RTI，機械無沖擊155 °C@Thickness 0.810 mm311 °F@Thickness 0.0319 inUL 746B可燃性(UL94)V-0@Thickness 0.810 mmV-0@Thickness 0.0319 inUL94加工性能額定值 (公制)額定值 (英制)測試方法加工（熔體）溫度270 - 290 °C518 - 554 °F干燥溫度120 °C248 °F干燥時間4.00 hour4.00 hour水分含量